We deal in all sizes is from 1mm to 100mm as per client's requirements.
Corten Steel Plates Nalin Girish Ispat LLP Across Pan India.
Corten
Steel is a high strength weathering steel. The word
“CorTen” is the trademark name given to a weathering
steel alloy material originally produced by United States
Steel. CorTen Steel is no longer
produced in the United States. In industrial specifications,
weathering steel is commonly known by the name “Cor
10.” This steel is available in sheets, plates,
coils, angles, channels, pipes and tubes, and is available
in the applicable equivalent ASTM specifications of
ASTM A588, A242, A606-4, A847 and A709-50W.
Since COR-TEN has excellent weather resistance, it can be
used without any coating.
It provides not only the economic effect of a reduction of
recoating cost, but an aesthetic effect with sedate color of
protective rust.
Corten steel
is a brown-orange steel. The coloration is due to the
self-protecting rust layer that naturally forms over time.
Once it has matured, this layer of metal oxide is called a «
patina ». Corten Steel is a metal that
changes over time under the influence of atmospheric
conditions. Due to its chemical properties, rusty corten
steel is also known as weathering steel and self-healing
steel. The corten steel is used for various types of welded,
bolted and riveted constructions e.g. steel frame
structures, bridges, tanks and containers, exhaust systems,
vehicles and equipment constructions
For more information about Corten Steel Plates or to discuss using it in your application, please contact Divyesh Shah or give us a call at +91 98201 27077 / +91 22315 18314
We deal in all sizes is from 1mm to 100mm as per client's requirements.
Material : Corten A,
Corten B , S355J0WP, S355J0W, S355J2W,
A588 Grade A, A588 Grade B, A242 Type 1
A242 Type 2, ASTM A606 Type 1 , ASTM
A606 Type 2
Thickness : 1.5mm – 100mm
Width : 1000mm – 3000mm
Length : 2500mm- 12000mm
Uses : Corten steel is
used in external and internal cladding
for any building, Bridges, Containers
and more usages.
| Grade | C % | Si % | Mn % | P % | S % | Cr % | V % | Ni % | Cu % |
| A588 Gr A | 0.19 | 0.30-0.65 | 0.80-1.25 | 0.04 | 0.05 | 0.40-0.65 | 0.02-0.10 | 0.40 | 0.25-0.5 |
| A588 Gr B | ≤0.20 | 0.15-0.50 | 0.75-1.35 | 0.040 | 0.050 | 0.40-0.70 | 0.01-0.10 | ≤0.50 | ≤0.50 |
| Grade | C | Mn | P | S | Si | Cr | Ni | Mo | Cu | Fe |
| IRSM 41-97 | 0.10 | 0.25-0.45 | 0.075-0.112 | 0.030 | 0.28-0.72 | 0.35-0.49 | 0.20-0.49 | – | 0.30-0.39 | – |
| Grade | C | Mn | Cr | Si | CEV | S | Cu | P |
| ASTM A242 TYPE 1 | Max 0.12 | Max 1 | 0.3-1.25 | Max 0.75 | Max 0.52 | Max 0.03 | 0.25-0.55 | 0.06 – 0.15 |
| ASTM A242 TYPE 2 | 0.20 Max | 1.35 Max | 0.3-1.25 | - | - | 0.05 | 0.20 Min | 0.04 |
| Grade | C | Si | Mn | P | S | Al | V | Cu | Cr | Ni |
| CORTEN A | 0.12 max | 0.25 - 0.75 | 0.20 - 0.50 | 0.07 - 0.15 | 0.030 max | 0.015 - 0.06 | - | 0.25 - 0.55 | 0.50 - 1.25 | 0.65 max |
| CORTEN B | 0.19 max | 0.30 - 0.65 | 0.80 - 1.25 | 0.035 max | 0.030 max | 0.020 - 0.06 | 0.02 - 0.10 | 0.25 - 0.40 | 0.40 - 0.65 | 0.40 max |
| S355J2W+N Chemical Composition | ||||||||||
| C | Si | Mn | P | S | Cr | Zr | Ni | Cu | Mo | CEV |
| 0.16 max. | 0.50 max. | 0.50 max. | 0.03 max. | 0.03 max. | 0.40-0.80 | 0.15 max. | 0.65 max. | 0.25-0.55 | 0.03 max. | 0.44 max. |
| Grade | C | Mn | Ph |
| ASTM A606-4 | 0.22-0.26 | 1.25-1.3 | 0.04-0.06 |
| Steel Grades |
C max |
Si max |
Mn |
P max |
S max |
Cu max |
Cr max |
Ni max |
V max |
Nb max |
Al min |
| A 709 Gr.50W | – | – | – | 0.035 | 0.035 | – | – | – | – | – | 0.020 |
|
Grade
Corten IRSM 41-97 |
C | Mn | P | S | Si | Cr | Ni | Mo | Cu | Fe |
| 0.10 | 0.25-0.45 | 0.075-0.112 | 0.030 | 0.28-0.72 | 0.35-0.49 | 0.20-0.49 | – | 0.30-0.39 | – |
| Grade | Thickness | Yield
Strength ReH[N/mm2]transv.min |
TensileStrength Rm[N/mm2]transv |
| ASTM A588 | 0mm-100mm | 340 MPa | 480 MPa |
| 102mm-127mm | 320 MPa | 460 MPa | |
| 127mm-203mm | 290 MPa | 430 MPa |
| Grade | Standard | Tensile Strength MPa | Yield Strength MPa | Elongation in 2 inches (min.) % |
| IRSM 41-97 | Indian Railways | 480 min345 | 340 min | 21 |
| Grade | Min. Yield Strength Mpa | Tensile Strength MPa | Impact | ||||||||
| A242 Type1 | Nominal Thickness (mm) | Nominal Thickness (mm) | degree | J | |||||||
| Thick mm | ≤16 |
>16 ≤40 |
>40 ≤63 |
>63 ≤80 |
>80 ≤100 |
>100 ≤150 |
≤3 | >3 ≤100 | >100 ≤150 | -20 | 27 |
| A242 Type1 | 355 | 345 | …. | …. | …. | …. | 510-680 | 470-630 | …. | ||
| A242 Type 2 | |||
|
Properties |
Conditions |
||
|
T (°C) |
Treatment |
||
| Density (×1000 kg/m3) | 7.7-8.03 |
25 |
|
| Poisson’s Ratio | 0.27-0.30 |
25 |
|
| Elastic Modulus (GPa) | 190-210 |
25 |
|
| Grade | Yield strength ReL (N/mm 2) Min. | Tensile Strength Rm (N/mm 2) Min. | Elongation A50% Min. |
| COR-TEN A | 345 | 485 | 20 |
| COR-TEN B | 345 | 485 | 19 |
| S355J2W+N Mechanical Properties | |||
| Yield Strength | Tensile Strength | Minimum Elongation A (Lo = 5.65 vSo) % | |
| 355 MPa | 510 - 680 MPa | 20 | |
| Grade | Tensile Strength ksi | Yield2% Offset ksi |
| ASTM A606 TYPE 4 | 50 | 70 |
| Grade |
Thick mm |
Yield[MPa] | Tensile [MPa] | Elongtation Min % |
reduction Min % |
HB | |||
| Steel Plate | Structural steel | ||||||||
| 8in[200mm] | 2in[50mm] | 8in[200mm] | 2in[50mm] | ||||||
| A 709 Gr.50W | ≤100 | 345min | 485min | 18 | 21 | 18 | 21J | … | |
| Grade | Standard | Tensile Strengtd MPa | Yield Strengtd MPa | Elongation in 2 inches (min.) % |
| IRSM 41-97 | Indian Railways | 480 min345 | 340 min | 21 |