WEAR RESISTANT STEEL PLATES

Wear Resistant Steel Plates is an abrasion-resistant steel with a nominal hardness of 400-600 HBW. Wear resistant steels combines good bendability and weldability with an option for guaranteed impact toughness. The products can be used in many different components and structures that are subject to wear. Offering you a complete choice of products which include wear resistant steel - 300 Brinell, wear resistant steel 400 brinell plates, 450 Brinell plates, 500 Brinell Plates, wear resistant steel - 700 Brinell, heavy wear resistant steel and hard steel plate.

Wear Resistant Plates have outstanding resistance to corrosion when exposed to different cyclic mild environments. It offers the best performance in warm chloride environments while resisting pitting and crevice corrosion.

The key quality for wear resistant steels is their hardness. We sell wear plate according to its hardness measured on the Brinnell Hardness Test- usually in 400HB grades.

400 HB steel is over 3 times harder than mild steel(120HB), but only a third as hard as stainless steel (150HB). Example uses are for construction machinery, skips, bulldozers and excavators, buckets and conveyors.

Steels with a hig HB rating (Briness Hardness) are intended for applications where wear or abrasion resistance is important. The benefit of using an abrasion resistant steel is that the plant, machinery or constructions working life can be extended considerably. This can significantly improve the reliability, durability and safety of structures and equipment. It also helps to reduce the maintenance costs associated with wear and breakdown of plant.

Wear Resistance Plates of various mills [ JFE (Japan Future Enterprise), Nippon, Salzgitter, Clabeque, Dillinger, etc ]

For more information about Wear Resistant Steel Plates or to discuss using it in your application, please contact Divyesh Shah or give us a call at +91 98201 27077 / +91 22315 18314

We deal in all Size is from 5mm ~ 120 mm as per client's requirements.

Wear Resistant Steel Plate Grades

• 300 Brinell Hardness Number
• 500 Brinell Hardness Number
• 400 Brinell Hardness Number
• 700 Brinell Hardness Number
• 450 Brinell Hardness Number
• Raex 300
• Raex 400
• Raex 450
• Raex 500
• Dillidur 325 L
• Dillidur 400
• Dillidur 450
• Dillidur 500
• Dillidur 550
• Dillidur 600
• Perdur 400
• Perdur 450
• Perdur 500
• Welton 400
• Welton 450
• Welton 500

Specification

Material : SUMIHARD, NICRODUR, WELTE, ABREX, ROCKSTAR, ROCKHARD, BRINAR, DUROSTAT, DILLIDUR, JFE EVERHARD
Thickness: 5mm to 150mm
Width: 1000mm - 2500mm
Length: 6000mm - 12000mm
Heat Treatment: N, Q+T

Chemical Properties Mechanical Properties

300 BHN 400 BHN 450 BHN 500 BHN 700 BHN

Grade	C	Si	Mn	P	S	Cr	Ni	Mo	B
300 BHN	0.18 %	0.7 %	1.70 %	0.025 %	0.015 %	1.50 %	0.40 %	0.50 %	0.005 %

400 BHN Plate	C	Si	Mn	P	S	Cr	Ni	Mo	B	CEV	CET
thickness mm	max %	max %	max %	max %	max %	max %	max %	max %	max %	typv	typv
3- 6	0.15	0.70	1.60	0.025	0.01	0.50	0.25	0.25	0.004	0.41	0.28
3-（8）	0.15	0.70	1.60	0.025	0.01	0.30	0.25	0.25	0.004	0.33	0.23
8 - 20	0.15	0.70	1.60	0.025	0.01	0.50	0.25	0.25	0.004	0.37	0.27
（20）-32	0.18	0.70	1.60	0.025	0.01	1.00	0.25	0.25	0.004	0.48	0.29
（32）-45	0.22	0.70	1.60	0.025	0.01	1.40	0.50	0.60	0.004	0.57	0.31
（45）-51	0.22	0.70	1.60	0.025	0.01	1.40	0.50	0.60	0.004	0.57	0.38
（51）-80	0.27	0.70	1.60	0.025	0.01	1.40	1.00	0.60	0.004	0.65	0.41
（80）-130	0.32	0.70	1.60	0.025	0.01	1.40	1.50	0.60	0.004	0.73	0.48

Grade	C *)	Si *)	Mn *)	P	S	Cr *)	Ni *)	Mo *)	B *)
Max %	Max %	Max %	Max %	Max %	Max %	Max %	Max %	Max %
450 BHN	0.26	0.7	1.6	0.025	0.01	1040	1050	0.6	0.005

500 BHN Plate	C	Si	Mn	P	S	Cr	Ni	Mo	B	CEV	CET
THICKNESS MM	MAX %	MAX %	MAX %	MAX %	MAX %	MAX %	MAX %	MAX %	MAX %	TYPV	TYPV
4-13	0.27	0.7	1.6	0.025	0.01	1.0	0.25	0.25	0.004	0.49	0.34
(13) -32	0.29	0.7	1.6	0.025	0.01	1.0	0.50	0.30	0.004	0.62	0.41
(32) -40	0.29	0.7	1.6	0.025	0.01	1.0	1.00	0.60	0.004	0.64	0.43
(40) -80	0.30	0.7	1.6	0.025	0.01	1.50	1.50	0.60	0.004	0.74	0.46

Grade	C *)(max %)	Si *)(max %)	Mn *)(max %)	P(max %)	S(max %)	Cr *)(max %)	Cu *)(max %)	Ni *)(max %)	Mo *)(max %)	B *)(max %)
700 BHN	0.20	0.60	1.60	0.020	0.010	0.80	0.30	2.0	0.70	0.005

300 BHN 400 BHN 450 BHN 500 BHN 700 BHN

Grade	Yield Strength Mpa	Tensile Strength Mpa	Elongation A	Impact Strength Charpy V 20J
300 BHN	900	1000	11	-40 C

Grade	Yield Strength	Tensile Strength	Brinell Hardness	Elongation	Reduction of Area
400 BHN	140,000 Psi	180,000 Psi	400BHN	15%	60%

450 BHN
Thickness	Hardness HBW	Typical yield strength MPa,
mm	min - max 1)	not guaranteed
3 - 80	425 - 475	1100 - 1300
(80) - 100	410 - 475	1050 - 1300
(100) - 130	390 - 475	1000 - 1300

500 BHN
Thickness	Hardness HBW	Typical yield strength MPa,
mm	min - max 1)	not guaranteed
4 - 32	470 - 530	1250
(32) - 103	450 - 540	1250

700 BHN
Thickness(mm)	Yield strength Rp0.2 (min MPa)Tensile strength Rm	Tensile strength Rm (MPa)	Elongation A5(min %)
4.0 – 53.0	700	780 – 930	14
53.1 – 100.0	650	780 – 930	14
100.1 – 160.0	650	710 – 900	14

Applications Industries

For Buckets

For Truck Bodies

Agriculture Equipment

Underground Mining

For Defense

For Mining